Bioplastics for Blown Film
PolyEarthylene® blown film grades serve as a sustainable, biobased, landfill biodegradable, and recyclable option for various blown film applications. These grades offer alternatives to petroleum-based polyethylene and can be used on any standard blown film line. PolyEarthylene® maintains all the performance characteristics comparable to those of petroleum-based polyolefins.
PEL FZ 196
Blown film grade of PolyEarthylene® suitable for single use and reusable bags.
Application:
Blown Film
Melt flow rate:
1.90 g/10 min (190°C, 2.16Kg)
Biodegradation resin timeline:
1-3 years
Type:
LLDPE
Biobased content:
64%
Recyclability:
Yes
PEL FZ 282
Blown film grade of PolyEarthylene® suitable for single use and reusable bags with a higher level of clarity than PEL FZ 196.
Application:
Blown Film
Melt flow rate:
1.61 g/10 min (190°C, 2.16Kg)
Biodegradation resin timeline:
1-3 years
Type:
LLDPE
Biobased content:
63%
Recyclability:
Yes
PEL FZ 311
Blown film grade of PolyEarthylene® suitable for general use film with high strength and cold temperature durability.
Application:
Blown Film
Melt flow rate:
0.89 g/10 min (190°C, 2.16Kg)
Biodegradation resin timeline:
1-3 years
Type:
LLDPE
Biobased content:
45%
Recyclability:
Yes
PEL FL 297
Blown film grade of PolyEarthylene® suitable for shrink film (To be using in conjunction with PEL FZ 299).
Application:
Blown Film
Shrink, Stretch, & Speciality Film
Shrink, Stretch, & Speciality Film
Melt flow rate:
0.20 g/10 min (190°C, 2.16Kg)
Biodegradation resin timeline:
1-3 years
Type:
LDPE
Biobased content:
30%
Recyclability:
Yes
PEL FZ 299
Blown film grade of PolyEarthylene® suitable for shrink film (To be using in conjunction with PEL FL 297).
Application:
Blown Film
Shrink, Stretch, & Speciality Film
Shrink, Stretch, & Speciality Film
Melt flow rate:
0.92 g/10 min (190°C, 2.16Kg)
Biodegradation resin timeline:
1-3 years
Type:
LLDPE
Biobased content:
50%
Recyclability:
Yes